Impeller hub φ1412*380
1,按KM007较平衡
(1)叶轮最大工作转速1490r/min
(2)平衡等级按G1.6级允许的残余不平衡量每面为4750g-mm,在两个面上配重
(3)平衡重厚度不大于10mm
2,焊缝质量按DIN8563的第三部分BS和BK的等级施工及检验
3,焊后应清除焊渣,并作出应力退火处理
4,焊接质量按JB/T10213-2000的规定
5,托盘,盖盘与轮毂焊接处焊缝应作100%探伤检查
6,加工完成后,彻底清理,不得留有杂物
叶轮为焊接结构,较其它结构叶轮重量比较轻,惯性矩也小.叶片和叶柄等组装件的离心力通过平面推力球轴承传递至叶轮的支承环上.叶轮组装件在出厂前已进行多次动平衡.
1, according to KM007 more balanced
(1) Maximum working speed of the impeller 1490r/min
(2) The balance level is 4750g-mm on each side according to the residual unbalance allowed by G1.6, and the weight is balanced on both sides
(3) The thickness of the balance weight is not more than 10mm
2. Weld quality shall be constructed and inspected according to the third part BS and BK of DIN8563
3, welding slag should be removed after welding, and stress annealing treatment
4, welding quality according to JB/T10213-2000 regulations
5, the welding seam of the tray, cover plate and wheel hub should be 100% inspection
6, after the completion of processing, thoroughly clean up, no debris left